Sheet        Thickness:0.1mm~3.5mm
Plate        Thickness:3.5mm~40.0mm
Bar         Dia 5.0mm~Dia180.0mm
Pipe         OD 120mm~8.0mm,ID 8.0~129mm
Wire         Dia 0.1mm-Dia5.0mm
Products Application                                   Â
They are usually used for making instruments, wireless elastic sense organs, bellows, diaphragms.
Description                                         Â
A precipitation hardenable Nickel-Iron-Chromium alloy having outstanding controllable thermoelastic coefficient characteristics and excellent oxidation resistance in high temperature atmospheres. The alloy can be processed to have a constant modulus of elasticity at temperatures ranging from -45 to +65oC (-50 to +150oF).
Parameter                                          Â
TABLE 1        Cross Reference                                                                     Â
Contury                     Name 1                   Name 2                              Â
Russia                      42HXTΙΟ                   H42XT                          Â
USA Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Ni-Span c902 Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Elinvar
Germany                    Ni-Span C
UK Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Ni-Span C
Japan                      Sumispan-3                 EL-3                               Â
Â
TABLE 2    Chemical Requirement                                       Â
 Element                                         Composition,%                         Â
C  ≤                                                 0.05
Si≤                                                 0.80
P≤                                                  0.020
S≤                                                  0.020
Mn≤                                                 0.80
Ni≤                                                 41.5-43.0
Cr                                                 5.20-5.80
TI Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â 2.3-2.70
Al                                                  0.5-0.8
FE                                                 remainder                                     Â
Notes:
1.the shape and dimensions of the alloys are in compliance with YB/T5256-1993
Â
TABLE 3       Physical Requirement                                              Â
Property                                                  Target                         Â
Density                                                     8.0        Â
Modulus of Elasticity(E/Empa)                               176500-191000
Shear eleasticity(G/MPa) Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â 63500-73500
Vickers Hardness(HV) Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â 350-450
Staturation induction density(B600/T) Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â 0.7
Mean Coefficient of Linear Expansion20-100ºC(10-6/K)                 8.5
Resistivity p/(Ω°m)                                             1.1                          Â
Â
TABLE 4 Â Â Â Â Â Â Yield Strengh(after the heat treatment)Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â
Delivery State                  Thickness/mm          Yield Stength/Mpa                    Â
Annealed                      0.50-2.50                 <685
Cold rolled                     0.50-1.00                 >885                                Â
Â
TABLE 5       The temperature coefficient of the modulus of elasticity           Â
 Aging Temperature/ºC       The temperature coefficient of the modulus of elasticityβE/(10-6/ºC)(-6~+80ºC)
                                     Cold Rolling                  Annealed                Â
500 Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â -38~15 Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â +18~+12
550 Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â -22~0 Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â +10~+35
600 Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â 0~+20 Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â +35~+55
650 Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â 0~+20 Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â +42~+64
700 Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â 0~+20 Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â +40~+60 Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â
750 Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â -4~+16 Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â +28~+50 Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â Â
Â
TABLE 6         Mechanical property requirement                                    Â
Shape     Delivery State    Thickness&Diameter/mm     Tensile Strengthòb/MPa    Elongationò(%)≥  Â
Strip       Annealed         0.20-0.50                   <885                    20
Wire       Cold Drawn       0.20-3.0                    >930               
Â
New upgraded Furniture Handle, high quality stainless steel. Layer of artificial grinding, plating, but also polished out as the mirror comparable to the effect. Thicker without price. Just gently wipe with water every day, you can be bright as a freshman. Grooved screw holes can make the screw tightly, not loose, do not detach. Suitable for modern style, neoclassical style, nordic style, such as different decoration style. We are perfect in every detail, and we do not miss even the bottom. Good quality, allowing you to use more at ease.
Furniture Handle
Furniture Handle,Cabinet Furniture,Door Hardware Drawer Pull,Stainless Steel Furniture Handle
Metfull Metal Products Co.,LTD. , http://www.metfull.com